ゴムの熱的性質
熱伝導率: ゴムは熱伝導率が低く、厚さが 25 mm の場合の熱伝導率は約 2.2~6.28 W/m 2.0 K です。 保温性に優れた素材です。 ゴムを微孔質やスポンジ状にすると、断熱効果がさらに向上し、熱伝導率は0.4~2.0ワットまで低下します。 使用中のヒステリシスロスによりゴム部品が発熱する場合がありますので、放熱には十分ご注意ください。
Thermal expansion: because there is a large free volume between rubber molecular chains, the internal rotation of its chain segments becomes easier when the temperature rises, which will make its volume larger. The linear expansion coefficient of rubber is about 20 times that of steel. This must be considered in the vulcanization model design of rubber products, because the linear size of rubber products will be 1.2~3.5% smaller than the model. For the same type of rubber, the hardness of the rubber compound and the content of raw rubber also have a greater impact on the shrinkage of the rubber compound. The shrinkage is inversely proportional to the hardness and is proportional to the rubber content. The order of shrinkage of various rubbers in theory is: fluororubber>silicone rubber>butyl rubber>nitrile rubber>neoprene>styrene butadiene rubber>天然ゴム。 ゴム製品を低温で使用する場合は、体積収縮の影響に特に注意が必要です。 例えば、オイルシールは収縮による漏れ、ゴムと金属の接着品は収縮による過大な応力が発生し、早期破損につながります。